硅渣和玻璃粉直接烧结制备多孔材料的气孔结构与力学性能

以硅渣和玻璃粉为原料,采用粉体直接烧结法制备多孔材料,研究了烧结温度(700~900℃)、烧结时间(15~120min)和升温速率(10~100℃·min^-1)对多孔材料表观密度、气孔率、物相组成、抗压强度的影响。结果表明:气孔结构均匀性随烧结温度的升高而降低;表观密度随烧结温度的升高先减小后增大,随保温时间的延长而增大,随升温速率的增大而减小,气孔率的变化趋势与表观密度的相反;多孔材料的主要物相为玻璃相和硅、SiC、SiO2、Ca2Al2SiO7等结晶相,且结晶度随烧结温度的升高而降低;抗压强度随烧结温度的升高呈先增大后减小的趋势;当烧结温度为750℃,升温速率为30℃·min^-1,烧结时间为30 min时,多孔材料的主晶相为硅和Ca2Al2SiO7,抗压强度最大(1.60MPa),表观密度为0.43g·cm^-3,气孔率为80%。     

凉感纤维织物导热系数影响因素的探讨

采用普通涤纶、含1%云母颗粒的涤纶(1%云母/涤纶)以及含5%云母颗粒的涤纶(5%云母/涤纶)三种材质,上机纬密采用200根/10 cm、300根/10 cm、400根/10 cm,组织采用平纹、斜纹、缎纹试织试样。通过Hot Disk热常数分析仪,采用正交试验及极差、方差分析,研究了纤维材质、上机纬密、组织对凉感纤维织物导热系数的影响。结果表明:在试验设置变量范围内,纤维材质对导热系数的影响显著,上机纬密、组织对导热系数的影响高度显著,影响因素从大到小顺序为上机纬密>组织>纤维材质。     

Effect of Moving Speed of Charged Metallic Spherical Electrode on Electrostatic Discharge

In this investigation, the nature of the electrostatic discharge (ESD) that occurs when a charged object moves toward a stationary grounded object is experimentally clarified. The spark lengths, discharge currents, and induced voltages in a magnetic probe were measured when a charged metallic spherical electrode connected to a 422 pF capacitor approached a stationary grounded object, which was the current target, for different moving speeds of the charged metallic spherical electrode in a range of 1 mm/s to 100 mm/s. The charge voltages of the capacitor were +6.5 kV and +10 kV. Based on the results, the average gap length shortened with the speed of the spherical electrode. The average peak values of the discharge current and the induced voltage were likely to increase with the speed of the spherical electrode. The average rise times of the discharge current and the induced voltage were likely to drop with the speed of the spherical electrode. The relation between the spark length and the discharge current due to the ESD can be explained qualitatively by using an equation derived from the spark resistance formula proposed by Rompe and Weizel.     

锰基富锂正极材料Li_(1.2)Ni_(0.2)Mn_(0.59)Co_(0.01)O_2的首次充放电曲线分析

采用溶胶-凝胶法制备了锰基富锂正极材料Li1.2Ni0.2Mn0.59Co0.01O2。在类似的实验条件下制备了3组样品。分别用3组共计13个样品作为正极、金属锂作为负极制备了扣式电池以研究其首次充放电曲线和Coulomb效率。发现首次充电时平台容量(CP)占总充电容量(CT)的比例为首次Coulomb效率的曲线函数。而首次放电时,在3.5 V两侧均有1个放电平台,其微分容量曲线(d Q/d U)中2个峰的峰值比(PB/PC)为首次Coulomb效率的线性函数。通过分析,提出一个模型来解释锰基富锂材料的首次充放电行为。     

Two-Dimensional Problem of a Crack in Thermoelectric Materials

The two-dimensional problem of a crack in thermoelectric materials is studied in this research. The general solution is derived based on the complex variable method. For the case of a crack subjected to remote electric current and heat flow, the solutions are obtained in closed-form. The results show that the fields of heat flow, electric current, and stress exhibit traditional square-root singularity at the crack tip. The remote electric current produces both type I and II stress intensity factor. Furthermore, the stress intensity factor has a linear relationship with the heat flux, but a non-linear relationship with the electric current.     

Numerical simulation of lithium‐ion battery performance considering electrode microstructure

A spatially resolved three‐dimensional microscale model of a lithium‐ion battery half‐cell is developed and applied to periodic electrode microstructures made up of spherical particles following a bidisperse particle size distribution. The geometries of the periodic unit cells are derived from discrete element simulations using periodic boundary conditions. Three different particle arrangements, which consist of two layered structures and one mixed particle array, as well as three different compression rates, are considered. In the study, the cathode is assumed to consist of LiMn₂O₄ as active material. Layered particle arrangements comprising the particle fraction of the smaller particle size in the region close to the separator are found to be beneficial especially for high‐rate applications. According to the simulation results, the high‐rate capability is reduced upon compression of the electrode microstructures. Copyright © 2015 John Wiley & Sons, Ltd.     

Intense-pulsed-light irradiation of Ag nanowire-based transparent electrodes for use in flexible organic light emitting diodes

Silver nanowire (AgNW) based transparent electrodes are inherently coarse and therefore typically are only ever weakly bonded to a substrate. A remarkable improvement in the characteristics of a AgNW network film has, however, been achieved through a simple and short process of irradiating it with intense pulsed light (IPL). This not only avoids any severe deterioration in the optical characteristics of the AgNW film, but also significantly improves its electrical conductivity, adhesion to a polymeric substrate, and ability to endure bending stress. Most important of all, however, is the finding that the surface roughness of AgNW networks can also be improved by radiation. In a series of measurements made of organic light emitting diodes fabricated using these treated electrodes, it was revealed that the leakage current can be notably reduced by IPL treatment.     

基于期权合约的战备物资储备激励机制研究

针对通用战备物资依托企业合同储备问题,从合作博弈的角度出发,引入期权合约理论,构建期权合约下合同储备激励机制模型。分析影响各方博弈主体策略选择的因素,对不同策略下参与主体双方的利润期望进行比较分析,确立期权合约理论下合理的期权价格范围,寻求军地双赢策略。实例分析表明,提出的方法具有可行性和有效性。     

Exploration of amorphous hollow FeOOH@C nanosphere on energy storage for sodium ion batteries

Sodium ion batteries (SIBs) have enjoyed a high profile in recent years and gradually been commercialized to supplement the lithium-ion batteries system. However, the large volume expansion of anode materials within discharging and low electrical conductivity hinder the application of SIBs. In this work, a FeOOH@C composite was synthesized with the use of hydrothermal method and pyrolyzing of polydopamine. The amorphous FeOOH exhibits a hollow spherical structure to offer free space for buffering the volumetric variation. Furthermore, the outer carbon served as a protective shell could maintain the sphere integrity and enhance the electrical conductivity. Hence, benefiting from the achieved synergy of the hollow architecture, amorphous structure and carbon shell, the composite presented a long cycle life (316 mA h g^?1 after 500 cycles at a current density of 100 mA g^?1 and 234.5 mA h g^?1 after 400 cycles at 2 A g^?1) and high-rate performance (180 mA h g^?1 at 5 A g^?1), revealing a potential to be a promising candidate for electrode material of SIBs.